Description
3M™ Scotch-Weld™ Epoxy Adhesive DP100 Plus Clear is a fast setting, two-part, 1:1 mix ratio mercaptan-cured epoxy adhesive. It is unique among fast setting mercaptan cure epoxies in that it combines high shear strength with good peel performance properties. Scotch-Weld epoxy adhesive DP100 Plus Clear is transparent and slightly flexible when cured.
Features:
- 4 Minute Work Life
- High Shear & Peel Strength
- Slightly Flexible When Cured
Overlap Shear Strength (OLS) vs. Temperature:
(Bonds cured 24 hours @ room temperature (RT) + 2 hrs @ 160°F [71°C])
|
Etched Aluminum |
3500 psi |
|
Sanded Aluminum (60 grit) |
1800 psi |
|
Cold Rolled Steel |
1700 psi |
|
Wood,Fir |
700 psi |
|
Glass, Borosilicate |
250 psi |
|
Glass, +3M™ Scotch-Weld™ Primer EC3901 |
300 psi |
|
Polycarbonate |
600 psi |
|
Acrylic |
300 psi |
|
Fiberglass |
1500 psi |
|
ABS |
280 psi |
|
PVC |
450 psi |
|
Polypropylene |
80 psi |
Rate of Strength Build-Up (OLS on Etched Aluminum) Bonds tested after:
|
1 hr @ RT |
600 psi |
|
6 hrs @ RT |
900 psi |
|
24 hrs @ RT |
1100 psi |
|
7 days @ RT |
2800 psi |
|
1 mo @ RT |
3400 psi |
Environmental Aging: (OLS on Etched Aluminum)Bonds tested after:
|
24hrsRT+ 2 hrs @ 160°F (71°C) |
3500psi |
|
24hrsRT+ 2 hrs @ 240°F (116°C) |
4500psi |
|
1 wk RT + 1 wk @ 90°F (32°C)/90% RH |
3900psi |
|
1 wk RT + 1 wk 248°F (120°C) |
4500psi |
|
1 wk RT + 1 wk H2O immersion |
3500psi |
Overlap shear (OLS) strengths were measured on1 in. wide 1/2 in. overlap specimens. These bonds were made individually using 1 in. x 4 in. pieces of substrate. The thickness of the bond line was 0.005-0.008 in. All strengths were measured at 70°F (21°C) except where noted. (Test per ASTM D 1002-72.)
The separation rate of the testing jaws was 0.1in. per minute for metals, 2 in. per minute for plastics and 20 in. per minute for rubbers. The thickness of the substrates were: steel, 0.060 in.; other metals, 0.05-0.064 in.; rubber, 0.125 in.; plastics, 0.125 in.
Overlap Shear Strength (OLS) vs. Temperature
(Bonds cured 24 hours @ room temperature (RT) + 2 hours @ 160°F [71°C])
|
Bonds tested at: |
|
|
-67°F(-55°C) |
3000psi |
|
70°F(21°C) |
3500psi |
|
120°F(49°C) |
750psi |
|
150°F(66°C) |
400psi |
|
180°F(82°C) |
200psi |
180° Peel Strength vs. Temperature
(Bonds cured 24 hours @ room temperature (RT) + 2 hours @ 160°F [71°C])
|
-67°F(-55°C) |
2 piw |
|
70°F(21°C) |
13piw |
|
120°F(49°C) |
15piw |
|
150°F(66°C) |
2 piw |
|
180°F(82°C) |
1 piw |
Solvent Resistance
|
|
OneHour/OneMonth |
|
Acetone |
A/A |
|
IsopropylAlcohol |
A/A |
|
FreonTF |
A/A |
|
FreonTMC |
A/A |
|
1,1,1-Trichloroethane |
A/A |
|
RMAFlux |
A/A |
|
Key: A - Unaffected, B - Slight Attack, C - Moderate/Severe Attack |
|
Exotherm
|
|
Max.Temp/TimetoReach |
|
2 gram mass |
128°F/6min. |
|
20grammass |
260°F/3min. |
12 Overlap shear (OLS) strengths were measured on1 in. wide 1/2 in. overlap specimens. These bonds were made individually using 1 in. x 4 in. pieces of substrate. The thickness of the bond line was 0.005-0.008 in. All strengths were measured at 70°F (21°C) except where noted. (Test per ASTM D 1002-72.)
The separation rate of the testing jaws was 0.1in.per minute for metals,2 in. per minute for plastics and 20 in. per minute for rubbers. The thickness of the substrates were: steel, 0.060 in.; other metals, 0.05-0.064 in.; rubber, 0.125 in.; plastics, 0.125 in.
13 T-peel strengths were measured on1 in. wide bonds at 73°F (23°C). The testing jaw separation rate was 20 inches per minute.
The substrates were 0.020in.thick.(TestsperASTMD 1876-61T.)
14 Solvent resistance was determined using cured (24hrs. RT + 2 hrs. 160°F [71°C]) samples (1/2 in. x 4 in. x 1/8 in. thickness) immersed in the test solvent for 1 hour and 1 month. After the allotted period of time, the sample was removed and visually examined for surface attack as compared to the control.
Key: A - Unaffected - no change to color or surface texture.
B - Slight attack - noticeable swelling of surface.
C - Moderate/severe attack - extreme swelling of surface.