Description
Permabond TA4610 is a 2-part, 1:1 toughened acrylic adhesive. It has been developed to bond low surface energy plastics such as polypropylene and polyethylene - with no primer or expensive surface treatment required. It can also be used to bond a wide variety of other materials such as metals and composite materials and ideal for bonding dissimilar surfaces.
TA4610 is a substitute / backup formula for these formulas:
- 3M DP8005
- 3M DP8010
- Scigrip SG400 LSE
Features and Benefits:
- Adhesion to a wide variety of substrates
- Thick Gel Formula, Thixotropic, Non-Sagging, Gap-Filling
- Full cure at room temperature
- Set time is 12-15 min
- Bonds to polyolefins
- No primer required
- No need to flame-treat or plasma treat-surfaces before bonding
- Excellent impact & sheer strength
- Excellent chemical resistance
Ideal Surfaces / Works With:
- Most Metals (Mild Steel, Stainless Steel, Aluminum, etc)
- Most Plastics & In particular the hard-to-bond Low-Energy Plastics
- Composites
- Carbon Fiber
- FRP (fiber reinforced plastics)
- GRP (glass reinforced plastics)
- ABS,
- Polycarbonate
- PVC
- PA6
- PET-G
- PE-P
- EPDM & Rubbers
- E- Coatings
- Polypropylenes (PPCO, PPHO, and related)
- Polyethlyenes (LLDPE, LDPE, MDPE, HDPE, UHMW, etc)
- PTFE / Nylon
Physical Properties of Uncured Adhesive
| TA4610 A | TA4610 B | |
| Chemical Composition | Methacrylate | Methacrylate |
| Color | Off-white | Almost colorless |
| Mixed Color | Off-white | |
| Viscosity @ 25°C | 200,000-500,000 mPa.s (cP) Thixo paste | 20,000-30,000 mPa.s (cP) |
| Specific gravity | 1.0 | 1.0 |
Typical Curing Properties
| Ratio to Use | 1 : 1 |
| Maximum gap fill (NB: Contains microparticles to control gap) | 1 mm (0.04 in) |
| Pot life (2g+2g) @23°C | 5-8 minutes |
| Fixture time (0.1 N/mm ² shear strength is achieved) @23°C | 12-15 minutes |
| Handling time (0.3 N/mm ² shear strength is achieved) @23°C | 40-50 minutes |
| Working strength @23°C | 6-8 hours |
| Full cure @23°C | 36-48 hours |
Comparable to 3M DP8005, DP 8010, and DP-8010